How does the deposited dose of oxide nanomaterials evolve in an in vitro assay?

Résultats de recherche: Contribution à un journal/une revueArticleRevue par des pairs


In this work, the evolution of some key physicochemical parameters of oxide engineered nanomaterial (ENM) dispersions was studied during an in vitro biological assessment. Commercial oxide ENMs, SiO and TiO , were dispersed in aqueous solutions (20 μg/mL) to A549 cells and N-hTERT keratinocytes and were assessed at several incubation times: 6, 24, 48, and 72 hours. The ENMs deposited dose and its particle size distribution (PSD) were followed each time. Centrifuge Liquid Sedimentation (CLS) measured the PSD and the ENMs deposited dose from a particle entity perspective, while Particle-Induced X-ray Emission (PIXE) measured the ENMs deposited dose from an elemental mass perspective. No significant variations in PSD were observed for SiO ENMs during incubation in A549 cells and TiO ENMs in both cell lines, while a continuous evolution of the PSD is observed for SiO in N-hTERT keratinocytes. The deposited dose for TiO ENMs remained stable and similar in both cell lines due to a smaller specific surface area and a higher quantity of primary particles present during incubation. It is concluded that the observed differences in the deposited dose are related to an interaction between the proteins present in the media and the ENMs specific surface.
langue originaleAnglais
Numéro d'article012013
Nombre de pages10
journalJournal of Physics : Conference Series
Numéro de publication1
Les DOIs
Etat de la publicationPublié - 2013

Empreinte digitale Examiner les sujets de recherche de « How does the deposited dose of oxide nanomaterials evolve in an in vitro assay? ». Ensemble, ils forment une empreinte digitale unique.

Contient cette citation