WO3/PANI核壳结构反蛋白石薄膜的电致变色性能

Liqi Jiang, Ke Wei, Lang Wang, Houdi Xiao, Jiuxiang Yang, Zhiyi Hu, Jing Liu, Yu Li, Mingyun Lyu, Baolian Su

Résultats de recherche: Contribution à un journal/une revueArticleRevue par des pairs

Résumé

A conductive polymer polyaniline(PANI) layer was introduced on the surface of the inverse opal structure tungsten trioxide(IO-WO3) film by the successive ionic layer adsorption and reaction, then a unique core-shell inverse opal structure WO3/PANI(IO-WO3/PANI) film was fabricated. The morphology, composition, and electrochemical behavior of the IO-WO3/PANI film were studied and compared with the IO-WO3 film. When the potential scan ranged from -0.6 V to 1.0 V, the IO-WO3/PANI composite film showed different colors under different voltage states, namely blue(1.0 V), green(0.2 V), light green(0 V) and blue-violet (-0.6 V). Compared with the IO-WO3 film, the electrochromic performance of the IO-WO3/PANI film is signi-ficantly improved. The coloring and fading response times are 3.8 and 6.14 s, respectively, and the color change efficiency(CE) value is 201.1 cm2/C. The improvement of electrochromic performance is mainly attri- buted to the formation of the donor-acceptor system and the hierarchically porous structure in the core-shell inverse opal, which enable rapid ion diffusion and provide a larger surface area for charge transfer reactions. The results show that the IO-WO3/PANI core-shell inverse opal film is a potential multicolor electrochromic material and has broad application prospects in the future.

Titre traduit de la contributionElectrochromic Property of the WO3/PANI Core-Shell Inverse Opal Structure Film
langue originaleChinois (traditionnel)
Pages (de - à)2996-3004
Nombre de pages9
journalGaodeng Xuexiao Huaxue Xuebao/Chemical Journal of Chinese Universities
Volume42
Numéro de publication9
Les DOIs
Etat de la publicationPublié - 10 sept. 2021
Modification externeOui

Empreinte digitale

Examiner les sujets de recherche de « WO<sub>3</sub>/PANI核壳结构反蛋白石薄膜的电致变色性能 ». Ensemble, ils forment une empreinte digitale unique.

Contient cette citation