T1 - Gold catalysts supported on ceria-modified mesoporous zirconia for low-temperature water-gas shift reaction
AU - Idakiev, V.
AU - Tabakova, T.
AU - Tenchev, K.
AU - Yuan, Z.-Y.
AU - Ren, T.-Z.
AU - Su, B.-L.
PY - 2012/2/1
Y1 - 2012/2/1
N2 - New gold catalytic system prepared on ceriamodified mesoporous zirconia used as water-gas shift (WGS) catalyst is reported. Mesoporous zirconia was synthesized using surfactant templating method through a neutral [C (EO) -Zr(OC H ) ] assembly pathway. Ceria modifying additive was deposited on mesoporous zirconia by deposition-precipitation method. Gold-based catalysts with different gold content (1-3 wt. %) were synthesized by deposition-precipitation of gold hydroxide on mixed metal oxide support. The supports and the catalysts were characterized by powder X-ray diffraction, high-resolution transmission electron microscopy, N adsorption analysis and temperature programmed reduction. The catalytic behavior of the gold-based catalysts was evaluated in WGS reaction in a wide temperature range (140-300 °C) and at different space velocities and H O/CO ratios. The influence of gold content and particle size on the catalytic performance was investigated. The WGS activity of the new Au/ceria-modified mesoporous zirconia catalysts was compared with that of gold catalysts supported on simple oxides CeO and mesoporous ZrO , revealing significantly higher catalytic activity of Au/ceria-modified mesoporous zirconia. A high degree of synergistic interaction between ceria and mesoporous zirconia and a positive modification of structural and catalytic properties by ceria have been achieved. It is clearly revealed that the ceria-modified mesoporous zirconia is of much interest as potential support for gold-based catalyst. The Au/ceria-modified mesoporous zirconia catalytic system is found to be effective catalyst for WGS reaction.
AB - New gold catalytic system prepared on ceriamodified mesoporous zirconia used as water-gas shift (WGS) catalyst is reported. Mesoporous zirconia was synthesized using surfactant templating method through a neutral [C (EO) -Zr(OC H ) ] assembly pathway. Ceria modifying additive was deposited on mesoporous zirconia by deposition-precipitation method. Gold-based catalysts with different gold content (1-3 wt. %) were synthesized by deposition-precipitation of gold hydroxide on mixed metal oxide support. The supports and the catalysts were characterized by powder X-ray diffraction, high-resolution transmission electron microscopy, N adsorption analysis and temperature programmed reduction. The catalytic behavior of the gold-based catalysts was evaluated in WGS reaction in a wide temperature range (140-300 °C) and at different space velocities and H O/CO ratios. The influence of gold content and particle size on the catalytic performance was investigated. The WGS activity of the new Au/ceria-modified mesoporous zirconia catalysts was compared with that of gold catalysts supported on simple oxides CeO and mesoporous ZrO , revealing significantly higher catalytic activity of Au/ceria-modified mesoporous zirconia. A high degree of synergistic interaction between ceria and mesoporous zirconia and a positive modification of structural and catalytic properties by ceria have been achieved. It is clearly revealed that the ceria-modified mesoporous zirconia is of much interest as potential support for gold-based catalyst. The Au/ceria-modified mesoporous zirconia catalytic system is found to be effective catalyst for WGS reaction.
UR - http://www.scopus.com/inward/record.url?scp=84861795126&partnerID=8YFLogxK
U2 - 10.1007/s10934-010-9441-x
DO - 10.1007/s10934-010-9441-x
M3 - Article
AN - SCOPUS:84861795126
SN - 1380-2224
VL - 19
SP - 15
EP - 20
JO - Journal of Porous Materials
JF - Journal of Porous Materials
IS - 1
ER -